WEKO3
アイテム
冷間加工後の熱処理によるSUS316FR ステンレス鋼の組織変化
https://doi.org/10.57375/00000035
https://doi.org/10.57375/00000035b0e02d88-0a8b-44c7-bcd5-9cf749268485
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
047-052.pdf (4.6 MB)
|
|
| Item type | 紀要論文 / Departmental Bulletin Paper(1) | |||||
|---|---|---|---|---|---|---|
| 公開日 | 2014-07-14 | |||||
| タイトル | ||||||
| タイトル | 冷間加工後の熱処理によるSUS316FR ステンレス鋼の組織変化 | |||||
| タイトル | ||||||
| タイトル | Change in Structure of SUS316FR Stainless Steel by Heat-treatment after Cold Working | |||||
| 言語 | en | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | SUS316FR | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | Hardness | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | X-ray Diffraction | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | Dislocation Density | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | Heat-treatment | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | Grain Size | |||||
| 資源タイプ | ||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||
| 資源タイプ | departmental bulletin paper | |||||
| ID登録 | ||||||
| ID登録 | 10.57375/00000035 | |||||
| ID登録タイプ | JaLC | |||||
| 著者 |
羽木, 秀樹
× 羽木, 秀樹× Hagi, Hideki |
|||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | The change in structure of SUS316FR stainless steel caused by heat-treatment after cold working was investigated on the basis of Vickers hardness test, X-ray diffraction, and SEM observation. At the heat-treatment temperature below 300℃, Vickers hardness, HV, increased slightly, and half-value width of X-ray diffraction peak decreased slightly. These phenomena result from the diffusion of interstitial impurities to dislocation core. Between 300℃ and 500℃, HV was approximately constant, and the half-value width decreased. These phenomena result from the rearrangement of dislocations. At temperatures above 500℃, both HV and the half-value width decreased. The decrease in HV and the half-value width was thought to be caused by re-crystallization with the heat-treatment and large decrease of dislocation density. By the heat-treatment above 700℃, grain size was grown. | |||||
| 書誌情報 |
福井工業大学紀要研究 号 44, p. 47-52, 発行日 2014-07-14 |
|||||
| 出版者 | ||||||
| 出版者 | 福井工業大学 | |||||
| 書誌レコードID | ||||||
| 識別子タイプ | NCID | |||||
| 関連識別子 | TF00008494 | |||||
| 著者版フラグ | ||||||
| 出版タイプ | VoR | |||||
| 出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||